Details of transitions of ZnI observed during the PLA of ZnO
Zinc (ZnI):[1]
Ground state: 1S Ionisation Potential: 9.39 eV
Transition |
E' (eV) |
E'' (eV) |
DE
(eV) |
Observed wavelength (nm) |
3P - 3D |
4.01 |
7.78 |
3.78 |
328.16 |
3P - 3D |
4.03 |
7.78 |
3.75 |
330.36 |
3P - 3D |
4.08 |
7.78 |
3.71 |
334.37 |
3P0 - 3S1 |
4.01 |
6.65 |
2.65 |
468.14 |
3P1 - 3S0 |
4.03 |
6.65 |
2.63 |
472.31 |
3P2 - 3S1 |
4.08 |
6.65 |
2.58 |
480.94 |
1P - 1D |
5.80 |
7.74 |
1.95 |
636.30 |
3D - 3P |
4.01 |
8.50 |
4.50 |
275.65 |
3D - 3P |
4.02 |
8.50 |
4.47 |
277.10 |
3S - 3P |
4.01 |
8.11 |
4.08 |
303.58 |
3S - 3P |
4.08 |
8.11 |
4.04 |
307.21 |
1S0 – 3P |
0.00 |
4.03 |
4.03 |
307.59 |
Details of transitions of ZnII observed during the PLA of ZnO
Zinc (ZnII):1
Transition |
E' (eV) |
E'' (eV) |
DE
(eV) |
Observed wavelength (nm) |
2S1/2 – 2P1/2 |
6.01 |
10.96 |
4.95 |
250.20 |
2S1/2 – 2P3/2 |
6.12 |
10.96 |
4.85 |
255.80 |
2D3/2 – 2F3/2 |
12.02 |
14.54 |
2.52 |
491.16 |
2D3/2 – 2F7/2,5/2 |
12.02 |
14.54 |
2.52 |
492.40 |
N/A |
|
|
2.10 |
589.43 |
2D5/2 – 2P1/2 |
12.57 |
14.63 |
2.06 |
602.12 |
2D5/2 – 2P1/2 |
14.63 |
15.90 |
1.27 |
610.25 |
N/A |
|
|
1.66 |
747.88 |
2P3/2 - 2S1/2 |
10.96 |
12.57 |
1.60 |
758.85 |
2S1/2 – 2P1/2 |
12.57 |
14.20 |
1.63 |
761.29 |
2P1/2 - 2S1/2 |
10.96 |
12.60 |
1.63 |
773.25 |
2S1/2 – 2P3/2 |
12.60 |
14.20 |
1.60 |
775.79 |
[1] NIST Atomic spectra database (http://physics.nist.gov/cgi-bin/AtData/main_asd) and references therein